| 固化前特性 | 項(xiàng)目 | 數(shù)值 | 固化后特性 | 項(xiàng)目 | 數(shù)值 |
| 外觀 | Aside透明液體 | 硬度 | 58shoreD | ||
| Appearamce | Hardness | ||||
| Bside透明液體 | 折射率 | 1.54 | |||
| Refractindex | |||||
| 密度 | Aside1.01 | 透光率(450nm/1mm) | 98% | ||
| Densityg/cm3 | Lighttransmittance | ||||
| Bside1.04 | 拉伸強(qiáng)度MPa | 7.5 | |||
| Tensilestrength | |||||
| 粘度 | Aside640 | 延伸率% | 20 | ||
| Viscaosity(25℃,mp.s) | Coefficientof | ||||
| extension | |||||
| Bside20000 | 體積膨脹系數(shù) | 190ppm/℃ | |||
| Volumeexpansion | |||||
| coefficient | |||||
| Mixed9800 | 體積電阻率 | >1×1014Ω.cm | |||
| Volumeresistiviy | |||||
| 可操作時(shí)間 | 180 | 介電常數(shù) | 3(60Hz) | ||
| Useaveilabetime(25℃,minutes) | Dielectricconstant | ||||
| 使用條件 | 混合比例 | 1:10 | 擊穿電壓 | 20~25Kv/mm | |
| MixingratioA:B | Punchthroughvoltage | ||||
| 標(biāo)準(zhǔn)固化條件 | 90℃×1h,150℃× | 彈性模量MPa | 152 | ||
| Standardcuringconditions | 3h | Modulusofealasticity |